ASTM B575 UNS N10276, Hastelloy C276
| Kelas | ASTM B575 UNS N10276, Hastelloy C276 - UNS N10276 - ALLOY C-276 (Ni / 15Cr / 16Mo / 4W) |
|---|---|
| Tipe | Coils, Plate, Strip, Sheet, Flat, Clad Plate, Rolling Plate, Flat Shim, Plain Sheet, Rolling Sheet Rolls, Blank (Lingkaran )`` Lembaran Datar, Lembaran Shim, anil lembut, kerak, dicukur, dianil, Pelat Checker, pelat tapak |
| Ketebalan Plat Hastelloy C276 Alloy | 0,3 hingga 1200 mm atau sesuai kebutuhan |
| C276 Hastelloy plate Width | 0-2500mm atau sesuai kebutuhan |
| ASTM B575 Alloy C276 Panjang Plat | 0-12mm atau sesuai kebutuhan |
| Permukaan pelat ASTM B575 Alloy C276 | BA, No. 3, No. 4, No. 6, No. 1, No. 2D, No. 2B, BA NO (8), No. 7, 2B, 2D, Pelat canai panas (HR), Lembaran canai dingin (CR), No.1 finish hot rolled ASTM B575 Alloy C276 Plate, SATIN (Bertemu dengan Pelapis Plastik), 2B, 1D, No.4, 8K, BA, garis rambut, sikat, satin, cermin dll. |
| Proses Pelat UNS N10276 Hastelloy C276 | Hot / Cold Rolled |
Analisis kimia
Bobot% (semua nilai maksimum kecuali jika rentang dinyatakan lain)
| Nikel | Keseimbangan | Mangan | 1.0 |
| Molibdenum | Maksimal 15,0 menit -17,0 | Karbon | 0.01 |
| Chromium | 14,5 menit-16,5 maks. | Vanadium | 0.35 |
| Besi | 4,0 menit-7,0 maks. | Fosfor | 0.04 |
| Tungsten | 3,0 menit-4,5 maks. | Sulfur | 0.03 |
| Kobalt | 2.5 | Silicon | 0.08 |
Peralatan mekanis
Nilai Khas pada 68 ° F (20 ° C)
| Kekuatan Hasil 0,2% Offset | Tarik Utama Kekuatan | Pemanjangan dalam 2 in. | Kekerasan | ||
|---|---|---|---|---|---|
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (maks.) |
| 41,000 | 283 | 100,000 | 690 | 40 | 100 Rockwell B |